PVC Plastic Wood Composite/TPE/PS Profile Extrusion Machine

Features

New revolution Wood Composite Material

  • Unique patented techology can be injection and extrusion molded sandwich, finished products has smooth surface and internal micro-bubbles nuclear characteristics, can enhance product value-added.
  • Products weight loss reached lightweight, whil le reducing the cost of the raw matcrials used.
  • Reduce the cooling time, improve production effciency.
  • Reduce the product shrinkage and warpage problem.
  • Do not use chemical blowing agent will not produce the freon gas of the impact on the environment through the European Union in 2013 disabled 6chemical blowing agent restriction.
  • Can be used in the nonchemical blowing agents can be added to plastic materials.
  • If didn't use physical foaming, the function eith general injection molding and extrusion machines are the same original raw materials of chemical blowing agents, can continul use the machine.
  • Lightweight the Product and Reduce the cost.
  • Innovation and Huge Progress.

APPLICATION

Specifications

Model CY-50PW CY-65PW CY-70PW CY-80PW CY-100PW
EXTRUDING CAPACITY (KGS/HR) 20 ~ 40 30 ~ 55 35 ~ 65 70 ~ 100 70 ~ 100
SCREW DIAMETER (MM) 50 m/m ø 65 m/m ø 70 m/m ø 80 m/m ø 100 m/m ø

PROCESS

PROCESS


PERFORMANCE CHARACTERISTICS

PROPERTY METHOD TEST RESULT
SPECIFIC DENSITY ASTM D648 700.00 kg/m³
MOISTURE CONTENT ASTM D648 1.70%
BENDING STRENGTH ASTM D1037-93 27.74 N/mm²
COMPRESSION TEMPERTURE ASTM D1037-93 11.6749 N/ mm²
SOFTENING TEMPERATURE ASTM D648 83.0℃
FIRE RETARDANT UL 94
SCREW WITHDRAWAL BS 6948:1989 91.85N